代理菲利普40玻纤PPS Ryton BR42B

详情描述：

代理菲利普40玻纤PPS Ryton BR42B
Ryton?BR42B 40%玻璃纤维增强聚苯硫醚化合物是专门配制的，可提供低摩擦系数和降低磨损率，用于需要低表面摩擦和/或磨损的应用场合。
Density / Specific Gravity
1.76
g/cm?
ASTM D792
Molding Shrinkage
 
 
 
Flow : 3.20 mm
0.20
%
 
Across Flow : 3.20 mm
0.50
%
 
Water Absorption (24 hr, 23?C)
0.020
%
ASTM D570
Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness
 
 
ASTM D785
M-Scale
97
 
 
R-Scale
117
 
 
Mechanical
Nominal Value
Unit
Test Method
Tensile Strength
 
 
 
--
186
MPa
ASTM D638
--
185
MPa
ISO 527-2
Tensile Elongation (Break)
1.6
%
ASTM D638, ISO 527-2
Flexural Modulus
14500
MPa
ASTM D790, ISO 178
Flexural Strength
 
 
 
--
269
MPa
ASTM D790
--
265
MPa
ISO 178
Compressive Strength
255
MPa
ASTM D695
Poisson's Ratio
0.40
 
 
Coefficient of Friction 3 (vs. Steel - Dynamic)
0.32
 
ASTM D3702
Wear Rate 3
1.60E-6
m/hr
ASTM D3702
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact
 
 
 
3.18 mm
91
J/m
ASTM D256
--
9.5
kJ/m?
ISO 180/A
    PPS平均分子量为0.4-0.5万，密度为1.3-1.8克每立方厘米，pps有十分有意的热性能。用玻纤增强后的热性能指标更高，它的连续使用温度达400度，pps的热稳定性优良，加热至500度时重量损失不明显，至700度时才会完全降解，它的力学性能随温度的升高下降很少，在232度经5000h的热老化后，其抗弯强度和抗拉强度还能保持50%以上。pps的抗拉强度、抗弯强度等性能在工程塑料中属中等水平，而伸长率和冲击强度却很低，因此在受力构件中使用pps通常加入添加剂，如玻纤、碳纤、填料等来增强其力学性能，pps通过这种改性后，主要力学性能，如抗拉性能、抗弯性能、压缩和冲击强度均有大幅度提高，伸长率却有下降，改性后的pps能在长期负荷和热负荷的作用下保持高的力学性能和尺寸稳定性，因而可应用于温度高的受力环境中。

代理菲利普40玻纤PPS Ryton BR42B