代理泰科纳50玻矿PPS FORTRON 6150T6

详情描述：

代理泰科纳50玻矿PPS FORTRON 6150T6
Fortron?6150T6是一种线性半结晶聚苯硫醚（PPS），专用级，用50%玻璃和矿物纤维加固。
Density
1.71
g/cm?
ISO 1183
Water Absorption (24 hr, 23?C)
0.050
%
ISO 62
Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness (M-Scale)
90
 
ISO 2039-2
Mechanical
Nominal Value
Unit
Test Method
Tensile Stress
155
MPa
ISO 527-2
Tensile Strain (Break)
1.7
%
ISO 527-2
Flexural Modulus
11200
MPa
ISO 178
Flexural Stress
205
MPa
ISO 178
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength (23?C)
8.0
kJ/m?
ISO 179/1eA
Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)
265
?C
ISO 75-2/A
CLTE
 
 
Internal Method
Flow
1.0E-5
cm/cm/?C
 
Transverse
4.0E-5
cm/cm/?C
 
Electrical
Nominal Value
Unit
Test Method
Volume Resistivity
2.0E 16
ohms?cm
IEC 60093
Electric Strength (3.00 mm)
16
kV/mm
IEC 60243-1
Relative Permittivity
 
 
IEC 60250
1 kHz
4.50
 
 
1 MHz
4.40
 
 
Dissipation Factor
 
 
IEC 60250
1 kHz
4.0E-3
 
 
1 MHz
5.0E-3
 
 
Arc Resistance
126
sec
ASTM D495
Comparative Tracking Index
150
V
IEC 60112
Fill Analysis
Nominal Value
Unit
Test Method
Melt Viscosity (310?C, 1000 sec^-1)
240000
mPa?s
ISO 11443
Additional Information
Nominal Value
Unit
Test Method
Color Number
HF2000/HD9100
 
 
 PPS平均分子量为0.4-0.5万，密度为1.3-1.8克每立方厘米，pps有十分有意的热性能。用玻纤增强后的热性能指标更高，它的连续使用温度达400度，pps的热稳定性优良，加热至500度时重量损失不明显，至700度时才会完全降解，它的力学性能随温度的升高下降很少，在232度经5000h的热老化后，其抗弯强度和抗拉强度还能保持50%以上。

代理泰科纳50玻矿PPS FORTRON 6150T6